Mae gan electrod dur di-staen austenitig math calsiwm titaniwm Cr26Ni21, metel tawdd ar dymheredd uchel 900-1100 ℃ ymwrthedd ocsideiddio rhagorol, defnydd deuol AC a DC.Technoleg weldio dda.Defnyddir yr un math o ddur di-staen gwrthsefyll gwres ar gyfer gweithio ar dymheredd uchel.Fe'i defnyddir hefyd ar gyfer weldio duroedd cromiwm caled mawr [fel Cr5Mo, Cr9Mo, Cr13, Cr28, ac ati] a dur annhebyg.
Cymhwysiad&Safon&Nodyn:
Cymhwysiad&Safon&Nodyn:
1. Yn addas ar gyfer cynhyrchion gwrthsefyll tymheredd uchel fel ffwrnais tymheredd uchel, offer golosg glo, ac ati, gellir ei ddefnyddio hefyd ar gyfer weldio deunydd annhebyg.
2. Y safon a gyfarfuom: GB/T983 E310-16, AWS A5.4 E310-16 & A5.4M E310-16, ISO3581-A:E(25 20) R 1 2, ISO3581-B:ES310-16, JIS Z3221 ES310-16
Mae electrod dur di-staen A402 wedi'i orchuddio â chalsiwm titaniwm Cr26Ni21 dur di-staen austenitig pur electrode.The metel gorchuddio wedi ymwrthedd ocsideiddio ardderchog ar 900 ~ 1100 ℃. Ac-dc defnydd deuol, wedi perfformiad weldio da broses.
Gellir rhannu electrod dur di-staen yn electrod dur di-staen cromiwm ac electrod dur di-staen nicel cromiwm, mae'r ddau fath hyn o electrod yn unol â'r safon genedlaethol, yn unol â darpariaethau GB/T983-1995 yr arholiad.Mae gan ddur di-staen cromiwm ymwrthedd cyrydiad penodol (asid ocsideiddio, asid organig, cavitation) ymwrthedd gwres a gwrthiant cyrydiad.Fe'i defnyddir fel arfer fel offer pŵer, cemegol, petrolewm a deunyddiau offer eraill.
Nodweddion
1. electrod dur di-staen calsiwm titaniwm, y prif gyfansoddiad yw 25% CR-20% Ni.
2. Sefydlog ymwrthedd tymheredd uchel, hyd at 1150 ℃.
3. Arc sefydlog, ffurfio hardd, crychdonnau mân, ychydig o dasgau, dad-slagio hawdd, ymwrthedd tân da croen cyffuriau, ymwrthedd stomatal da.
Pwyntiau i gael sylw:
Rhaid cael gwared ar olew arwyneb metel sylfaen, llwch a manion.Dylid glanhau'r wythïen weldio â brwsh dur di-staen.Mae un ochr i ffiliadau haearn wedi'u cymysgu â'r metel weldio yn effeithio ar ansawdd y weldio.Pan fydd yr electrod wedi'i wehyddu, dylai lled y gwehyddu fod o fewn 2.5 gwaith diamedr yr electrod.Rhaid i'r defnydd o electrod arian fod yn 250-300 ℃ sych 60 munud, pan gaiff ei ddefnyddio i dynnu swm bach i'r silindr sychu inswleiddio 100-150 ℃, cyflawni'r swm electrod i 4 awr yn briodol.
Cwmni a Ffatri
Cyflwyniad cyfansoddiad cynnyrch a phriodweddau mecanyddol
CYDRADDOLDEB CEMEGOL:
| ALLOY(wt%) | C | Mn | Si | Cr | Ni | Mo | P | S | Cu |
| RHEOLAU GB/T | 0.08-0.20 | 1.0-2.5 | 0.75 | 25.0-28.0 | 20.0-22.5 | 0.75 | 0.030 | 0.03 | 0.75 |
| RHEOLAU AWS | 0.08-0.20 | 1.0-2.5 | 0.75 | 25.0-28.0 | 20.0-22.5 | 0.75 | 0.030 | 0.03 | 0.75 |
| GWERTH ENGHREIFFTIOL | 0. 097 | 2.25 | 0.4 | 26.2 | 21 | 0.3 | 0.026 | 0.004 | 0.05 |
EIDDO MECANYDDOL:
| EIDDO | CRYFDER YIELD(MPa) | CRYFDER ESTYNIAD(MPa) | TRINIAD GWRES ℃ xh | GWERTH IMAPACT J/℃ | ELONGATION(%) | |||||||||
| RHEOLAU GB/T | - | 550 | - | - | 25 | |||||||||
| RHEOLAU AWS | - | 550 | - | - | 30 | |||||||||
| GWERTH ENGHREIFFTIOL | - | 600 | - | - | 35 | |||||||||
PARAMEDRAU WELDIO A ARGYMHELLIR:
| MANYLEBAU DIAMETER(mm) | 2.0*250 | 2.6*300 | 3.2*350 | 4.0*350 | 5.0*350 | |||||||
| TRYDAN (Amp) | H/W | 50-75 | 70-95 | 80-120 | 110-160 | 160-190 | ||||||
| O/W | 20-50 | 45-80 | 70-110 | 90-135 | - | |||||||
MANYLION PACIO:
| PENODIAD | HYD | PCS/1KG | PWYSAU/1KG | |||
| 2.0mm | 300mm | 79PCS | 2KG | |||
| 2.6mm | 300mm | 48PCS | 2KG | |||
| 3.2mm | 350mm | 27PCS | 5KG | |||
| 4.0mm | 350mm | 16PCS | 5KG | |||
| 5.0mm | 350mm | 12PCS | 5KG | |||
NODYN:
H/W: weldio safle llorweddol
O/W: weldio sefyllfa uwchben
Achosion Nodweddiadol
Tystysgrif
Cyflwyniad cyfansoddiad cynnyrch a phriodweddau mecanyddol
CYDRADDOLDEB CEMEGOL:
| ALLOY(wt%) | C | Mn | Si | Cr | Ni | Mo | P | S | Cu |
| RHEOLAU GB/T | 0.08-0.20 | 1.0-2.5 | 0.75 | 25.0-28.0 | 20.0-22.5 | 0.75 | 0.030 | 0.03 | 0.75 |
| RHEOLAU AWS | 0.08-0.20 | 1.0-2.5 | 0.75 | 25.0-28.0 | 20.0-22.5 | 0.75 | 0.030 | 0.03 | 0.75 |
| GWERTH ENGHREIFFTIOL | 0. 097 | 2.25 | 0.4 | 26.2 | 21 | 0.3 | 0.026 | 0.004 | 0.05 |
EIDDO MECANYDDOL:
| EIDDO | CRYFDER YIELD(MPa) | CRYFDER ESTYNIAD(MPa) | TRINIAD GWRES ℃ xh | GWERTH IMAPACT J/℃ | ELONGATION(%) | |||||||||
| RHEOLAU GB/T | - | 550 | - | - | 25 | |||||||||
| RHEOLAU AWS | - | 550 | - | - | 30 | |||||||||
| GWERTH ENGHREIFFTIOL | - | 600 | - | - | 35 | |||||||||
PARAMEDRAU WELDIO A ARGYMHELLIR:
| MANYLEBAU DIAMETER(mm) | 2.0*250 | 2.6*300 | 3.2*350 | 4.0*350 | 5.0*350 | |||||||
| TRYDAN (Amp) | H/W | 50-75 | 70-95 | 80-120 | 110-160 | 160-190 | ||||||
| O/W | 20-50 | 45-80 | 70-110 | 90-135 | - | |||||||
MANYLION PACIO:
| PENODIAD | HYD | PCS/1KG | PWYSAU/1KG | |||
| 2.0mm | 300mm | 79PCS | 2KG | |||
| 2.6mm | 300mm | 48PCS | 2KG | |||
| 3.2mm | 350mm | 27PCS | 5KG | |||
| 4.0mm | 350mm | 16PCS | 5KG | |||
| 5.0mm | 350mm | 12PCS | 5KG | |||
NODYN:
H/W: weldio safle llorweddol
O/W: weldio sefyllfa uwchben