Aloeon nicel Llawlyfr electrod ENi-1 gwneuthuriad saernïo weldio
CYDRADDOLDEB CEMEGOL:
| ALLOY(wt%) | C | Mn | Si | Ni | Fe | Ti | Cu | P | S |
| RHEOLAU GB/T | 0.10 | 0.75 | 1.20 | ≥92 | 0.70 | 1.0-4.0 | 0.20 | 0.02 | 0.015 |
| RHEOLAU AWS | 0.10 | 0.75 | 1.25 | ≥92 | 0.75 | 1.0-4.0 | 0.25 | 0.03 | 0.02 |
| GWERTH ENGHREIFFTIOL | 0.046 | 0.06 | 0.82 | 95.5 | 0.12 | 2.7 | 0.01 | 0.007 | 0.001 |
EIDDO MECANYDDOL:
| EIDDO | CRYFDER YIELD(MPa) | CRYFDER ESTYNIAD(MPa) | GWERTH IMAPACT J/℃ | ELONGATION(%) | ||||
| RHEOLAU GB/T | 200 | 410 | - | 18 | ||||
| RHEOLAU AWS | - | 410 | - | 20 | ||||
| GWERTH ENGHREIFFTIOL | 310 | 435 | - | 29 | ||||
PARAMEDRAU WELDIO A ARGYMHELLIR:
| MANYLEBAU DIAMETER(mm) | 2.6*300 | 3.2*350 | 4.0*350 | |||||||
| TRYDAN (Amp) | H/W | 65-95 | 70-115 | 95-145 | ||||||
Electrod llaw titaniwm-calsiwm, cyfansoddiad enwol (y cant yn ôl pwysau) yw 95Ni-2.5Ti.
Arc sefydlog, ffurfio hardd, ychydig o sblash, tynnu slag hawdd, ymwrthedd mandylledd da.
Mae gan y metel asio briodweddau mecanyddol da, ymwrthedd gwres, ymwrthedd cyrydiad, ymasiad a gwrthiant crac.
Defnyddir deunyddiau weldio cyfres dur Cr-Mo a deunyddiau weldio arwyneb electrod yn eang mewn offer mireinio petrolewm
-
Tancer Suez 158,000 tunnell
Supercore SG
CYDRADDOLDEB CEMEGOL:
| ALLOY(wt%) | C | Mn | Si | Ni | Fe | Ti | Cu | P | S |
| RHEOLAU GB/T | 0.10 | 0.75 | 1.20 | ≥92 | 0.70 | 1.0-4.0 | 0.20 | 0.02 | 0.015 |
| RHEOLAU AWS | 0.10 | 0.75 | 1.25 | ≥92 | 0.75 | 1.0-4.0 | 0.25 | 0.03 | 0.02 |
| GWERTH ENGHREIFFTIOL | 0.046 | 0.06 | 0.82 | 95.5 | 0.12 | 2.7 | 0.01 | 0.007 | 0.001 |
EIDDO MECANYDDOL:
| EIDDO | CRYFDER YIELD(MPa) | CRYFDER ESTYNIAD(MPa) | GWERTH IMAPACT J/℃ | ELONGATION(%) | ||||
| RHEOLAU GB/T | 200 | 410 | - | 18 | ||||
| RHEOLAU AWS | - | 410 | - | 20 | ||||
| GWERTH ENGHREIFFTIOL | 310 | 435 | - | 29 | ||||
PARAMEDRAU WELDIO A ARGYMHELLIR:
| MANYLEBAU DIAMETER(mm) | 2.6*300 | 3.2*350 | 4.0*350 | |||||||
| TRYDAN (Amp) | H/W | 65-95 | 70-115 | 95-145 | ||||||
Ysgrifennwch eich neges yma a'i hanfon atom