CYDRADDOLDEB CEMEGOL:
| ALLOY(wt%) | C | Mn | Si | Cr | Ni | Fe | Nb | Mo | P | S |
| RHEOLAU GB/T | - | - | - | - | - | - | - | - | - | - |
| RHEOLAU AWS | 0.10 | 0.50 | 0.50 | 20.0-23.0 | ≥58.0 | 5.00 | 3.15-4.15 | 8.0-10.0 | 0.02 | 0.02 |
| GWERTH ENGHREIFFTIOL | 0.015 | 0.25 | 0.3 | 22 | 64.00 | 0.3 | 3.3 | 9.5 | 0.0005 | 0.0005 |
EIDDO MECANYDDOL:
| EIDDO | CRYFDER YIELD(MPa) | CRYFDER ESTYNIAD(MPa) | GWERTH IMAPACT J/℃ | ELONGATION(%) | ||||
| RHEOLAU GB/T | - | - | - | - | ||||
| RHEOLAU AWS | - | 690 | - | 25 | ||||
| GWERTH ENGHREIFFTIOL | - | 760 | 80/- 196 | 32 | ||||
PARAMEDRAU WELDIO A ARGYMHELLIR:
| MANYLEBAU DIAMETER(mm) | 1.2 | ||||
| Folt | 25-34 | ||||
| Amp | 150-250 | ||||
| Hyd estyniad sych (mm) | 15-25 | ||||
| Llif nwy (l/munud) | 20-25 | ||||
Y cyfansoddiad enwol oedd 60%Ni-22%Cr-9%Mo-3%Fe-3.6%Nb.
Mae perfformiad effaith tymheredd isel -196 ° C yn ardderchog.
Mae'r arc yn feddal ac yn sefydlog, llai o sblash, ffurfio hardd, tynnu slag da, bwydo gwifren sefydlog, gyda pherfformiad proses weldio rhagorol.
-
Cais pŵer thermol
-
Qinghai Youjian Wunan Oilfield
-
Llong cynhwysydd 20000TEU
CYDRADDOLDEB CEMEGOL:
| ALLOY(wt%) | C | Mn | Si | Cr | Ni | Fe | Nb | Mo | P | S |
| RHEOLAU GB/T | - | - | - | - | - | - | - | - | - | - |
| RHEOLAU AWS | 0.10 | 0.50 | 0.50 | 20.0-23.0 | ≥58.0 | 5.00 | 3.15-4.15 | 8.0-10.0 | 0.02 | 0.02 |
| GWERTH ENGHREIFFTIOL | 0.015 | 0.25 | 0.3 | 22 | 64.00 | 0.3 | 3.3 | 9.5 | 0.0005 | 0.0005 |
EIDDO MECANYDDOL:
| EIDDO | CRYFDER YIELD(MPa) | CRYFDER ESTYNIAD(MPa) | GWERTH IMAPACT J/℃ | ELONGATION(%) | ||||
| RHEOLAU GB/T | - | - | - | - | ||||
| RHEOLAU AWS | - | 690 | - | 25 | ||||
| GWERTH ENGHREIFFTIOL | - | 760 | 80/- 196 | 32 | ||||
PARAMEDR WELDIO ARGYMHELLOLS:
| MANYLEBAU DIAMETER(mm) | 1.2 | ||||
| Folt | 25-34 | ||||
| Amp | 150-250 | ||||
| Hyd estyniad sych (mm) | 15-25 | ||||
| Llif nwy (l/munud) | 20-25 | ||||